HS-1013C-P Unsaturated Polyester Resin
Principal Properties & Application：
HS-1013C-P is an unsaturated polyester resin specially used for the production of flame-retardant lighting panels, which has good light transmittance, mechanical strength, flame-retardant properties, good weathering and yellowing resistance. It is suitable for mechanism/hand lay-up process.
n Specifications of liquid resin：
Item | Unit | Standard Requirements | Test Method |
Appearance | ―― | Purple-red transparent liquid | GB/T8237.6.1.1 |
Viscosity | 25℃, CP | 180-260 | GB/T7193.4.1 |
SPI-GT | min | 0.5 -1.5 | GB/T 7193.4.4 |
SPI-CT | min | 1.8 - 3.0 | GB/T 7193.4.4 |
SPI-PET | ℃ | 175-210 | GB/T 7193.4.4 |
To test the SPI curing characteristics, the curing system is: Curing agent M-50: 1.2 %
n Physical properties of Casting(for reference only)：
Item | Unit | Test Value | Test Method |
Tensile Strength | MPa | 55 | GB/T 2568 |
Elongation at Break | % | 3.8 | GB/T 2568 |
Bending Strength | MPa | 107 | GB/T 2570 |
Heat Distortion Temperature | ℃ | 63 | GB/T 1634 |
Oxygen index | % | 26 | GB/T 3854 |
Note:
1) Pouring system according to GB/T 8237-2005, curing system: curing agent M-50: 2%;
2) Curing system after casting is: room temperature (24 h) + 60℃ (3 h) + 100℃ (2 h).
Caution:
1, Transportation should be in accordance with the State Council “Regulations on the Safe Management of Dangerous Chemicals”, Chapter V of the safety regulations on the transportation of chemical hazardous substances. The product should be stored in a cool place under 25℃, avoiding fire, isolating heat source, and sealed to prevent moisture intrusion and volatilization of the monomer. the shelf life of the product is 3 months under 25℃.