Principal Properties & Application :
HS-11080ssk est unsaturated polyester resinae pro SMC / BMC, praesertim ex malefice anhydride et vexillum Glycols. Hoc features princeps reactivity, relative altum viscositas et bonum crassis proprietatibus. Cum in conjunction cum humilis-DECREMENTUM additives ut HS-(IX) DCCCXVII et HS, 9819a, potest producendum SMC / BMC products cum-gradu superficiem qualis. Est idoneam in-gradu superficiem automotive partes electrica coil encapsulation et aliis applications.
Specifications liquida resina:
Item | Vexillum iudicium | Test modus |
Species | Lumen flavo transparent liquidum | GB / T 8237.6.1.1 |
Viscosity (XXV ℃, CP) | 1900-2500 | GB / T 7193.4.1 |
Spi-GT (min) | 3.5-6.5 | DB001-D-HK |
Spi-CT (min) | 4.5-7.5 | DB001-D-HK |
Spi-pet (℃) | 230-260 | DB001-D-HK |
Acidum valorem (mgkoh / g) | 13.0-16.0 | GB / T MMDCCCXCV |
Solidum content (%) | 65.5-68.5 | GB / T 7193.4.3 |
Color numerus | ≤ III | DB036 DB036 |
Aqua contentus (%) | ≤ 0.125 | DB007-D-HK |
Ratio in SPI Test: Bpo crustulum II%.
Physica proprietatibus dejicientes (nam tantum):
Item | Unitas | Test valorem | Test modus |
Tensile vires | MPA | 48 | GB / T MMDLXVIII |
Tensile modulus | MPA | 3000 | GB / T MMDLXVIII |
Effrego elongatio | % | 1.4 | GB / T MMDLXVIII |
Flacalis fortitudinem | MPA | 86 | GB / T MMDLXX |
Flexural modulum | MPA | 3300 | GB / T MMDLXX |
Impulsum vires | KJ / M2 | 7 | GB / T MMDLXXI |
HDT | ℃ | 135 | GB / T MDCXXXIV |
Durness (Barcol 934-1) | - | 49 | GB / T MMMDCCCLIV |
Nota:
I) et mittens factum est secundum GB / T8237; Curing Ratio: Accelerator 0.6% Co-NAPH: 1.0%; Hardener Akzo M-L: I%;
II) Post curing: Rt × 24hrs + LX ℃ × 3hrs + CX ℃ × 2hrs