Principal Properties & Application:
HS-1010B est quaedam unsaturated polyester resina quod est in productione frp lucens laminam. Et FRP factum est bonum wideld, mechanica vires, diaphanum, et anti-canus perficientur cum patere ad ultraviolet. HS-1010B apta utraque apparatus et manus laicus modum.
Specifications liquida resina:
Item | Vexillum iudicium | Test modus | Adnotatio |
Species | Lux flavo Liquid transparent | HK-F-TM-00 |
|
Colo | ≦ L | HK-F-TM-I | Hazen |
Viscosity (XXV ℃, CP) | 120-190 | HK-F-TM-III | November ad March |
180-250 | HK-F-TM-III | Aprilis ut Maii, Septembris ad October |
250-350 | HK-F-TM-III | June ad August |
* Gel tempore (XXV ℃, min) | 9.0-13.0 | HK-F-TM, X |
|
* Curing Ratio in GT Test: Accelerator KC: II%; Hardener Akzo M-L: II%.
Physica proprietatibus dejicientes (nam tantum):
Item | Unitas | Test valorem | Test modus |
Tensile vires | MPA | 65 | GB / T MMDLXVIII |
Tensile modulus | MPA | 3550 | GB / T MMDLXVIII |
Effrego elongatio | % | 1.9 | GB / T MMDLXVIII |
Flacalis fortitudinem | MPA | 112 | GB / T MMDLXX |
Flexural modulum | MPA | 3650 | GB / T MMDLXX |
Impulsum vires | KJ / M2 | 10.5 | GB / T MMDLXXI |
HDT | ℃ | 78 | GB / T MDCXXXIV |
Durness (Barcol 934-1) | - | 46 | GB / T MMMDCCCLIV |
Note: I) Curing System: 0.6% co-NAPH I%; Mekp I%;
II) Post curing: Rt × 24hrs + LX ℃ × 3hrs + C ℃ × 2hrs.