N Principal Properties & Application :
HS-MD est unsaturated polyester resin propter SMC / BMC Applications. Hoc est ex Maleic Anhydride et vexillum Diols ut pelagus rudis materiae. Hoc resinae praebet princeps reactivity, medium viscositas, et optimum crassitate stabilitatem. Cum combined cum humilis DECREMENTUM agentibus ut HS, (IX) DCCCXCII, HS-(IX) DCCCXII, et HS-(IX) DCCCXIX, producit princeps superficiem species SMC / BMC products.
n cubits of liquida resina :
Item | Unitas | Vexillum iudicium | Test modus |
Species | --- | Pallide flavo transparent liquido | GB / T 8237.6.1.1 |
Viscosity | XXV ℃ , MPa.s | 1450-1750 | GB / T 7193.4.1 |
Spi-GT | min | 4.0.-8.0 | HK -D- DB001 |
Spi-CT | min | 5.5-10.5 | HK -D- DB001 |
Spi-pet | ℃ | 220-260 | HK -D- DB001 |
Acidum valorem | MGKOH / G | 13-19 | GB / T MMDCCCXCV |
Solidum contentus | % | 63-68 | GB / T 7193.4.3 |
Humor | % | ≤0.15 | HK -D- DB007 |
Index | --- | ≤80 | HK -D- DB036 |
Nota: Spi : Bpo Crustulum II%.
N Physical proprietatibus c Asting (quia non referat) :
Item | Unitas | Mensuratur valorem | Test modus |
Tensile viribus | MPA | 50 | GB / T 2568 |
Tensile modulus | MPA | 2900 | GB / T MMDLXVIII |
Elongatio ad confractus | % | 1.2 | GB / T MMDLXVIII |
Flacalis fortitudinem | MPA | 90 | GB / T 2570 |
Flexural modulum | MPA | 3300 | GB / T MMDLXX |
Barcol Hardness | --- | 49 | GB / T 3854 |
HDT | ℃ | 130 | GB / T 1634 |
Nota :
I) Projiciens sample praeparatio sequitur GB / T (VIII) CCXXXVII cum curatio ratio: 0.6% Co-NAPH 1,5%, AKZO M-L 1.5% ..；
II) curing processus post casting: XXIV horas ad locus temperatus + III horas ad LX ° C + II horas ad CX ° C.
N Operam :
Diam in translationem, quod productum est propinquos meos cum praescripta de ordinationibus in salutem procuratio de ancipitia chemicals (CAPUT V, ordinationes in onerariis et tractantem de ancipitia chemicals) a publica consilio. Quod productum debet condita in a frigus, opacum est infra XXV ° C, a fontibus ignitionis et semotus a calore fontibus. Signari ne humorem intrusionem et volatilizationis monomers. Et productum habet fasciae vita III mensibus cum repono ad temperaturis infra XXV ° C.